This Article Full Text (PDF) All Versions of this Article: 0892705709091859v1 22/6/585    most recent References Alert me when this article is cited Alert me if a correction is posted Services Email this article to a friend Similar articles in this journal Alert me to new issues of the journal Add to Saved Citations Download to citation manager Request Permissions Request Reprints Add to My Marked Citations Citing Articles Citing Articles via Scopus Google Scholar Articles by Alsewailem, F. D. Social Bookmarking                         What's this?

On the Thermal Expansion Behavior of Polystyrene/Polyethyleneterephthalate Blend Systems: Experimental Study

Petroleum and Petrochemical Research Institute King Abdulaziz City for Science and Technology (KACST) P.O. Box 6086, Riyadh 11442, Kingdom of Saudi Arabia, fsewailm{at}kacst.edu.sa

Thermal expansion behavior defined as the percentage of dimensional change upon heating for the blend systems of polystyrene/polyethyleneterephthalate has been investigated in this study. General purpose polystyrene (PS) and high impact polystyrene (HIPS) were blended with polyethyleneterephthalate (PET) at a weight ratio of (15/85). The dimensional change of the neat and blended polymers versus temperature is measured by a thermomechanical analyzer using an expansion probe. The study investigates thermal expansion behavior of the PS/PET and HIPS/ PET blend systems under various conditions of heating rate, load, and heating regime. Higher thermal expansion values for the neat polymers and the blends were observed at lower heating rate, i.e., 5°C/min, while increasing load did not seem to affect thermal expansion behavior of the materials except for neat PET and HIPS/ PET blend system at higher temperature range, i.e., beyond T_g of PET and near softening temp of HIPS, where thermal expansion values decreased as load increased. Neat polystyrenes exhibited noticeable thermal expansion and contraction behavior when tested isothermally. The blend systems formulated and tested in this study, which consisted 15/85 wt% of both PS/PET and HIPS/PET, have proven to be more thermally stable and have better thermal expansion behaviors in both heating regimes used, i.e., nonisothermal and isothermal, than those behaviors observed for the neat polymers especially the minor phase, i.e., the polystyrenes.

Key Words: polystyrene • polyethyleneterephthalate • thermal expansion.

This version was published on November 1, 2009

Journal of Thermoplastic Composite Materials, Vol. 22, No. 6, 585-604 (2009)
DOI: 10.1177/0892705709091859